ASTM A312 TP304L Stainless Steel Pipe (SS Pipe), 32mm*1.50mm*8750mm Beveled End.

316 and 317 stainless steel (317 stainless steel properties see below) are molybdenum-containing stainless steel. The molybdenum content in 317 stainless steel is slightly better than that in 316 stainless steel. Because of the molybdenum in the steel, the total performance of the steel is better than that of 310 and 304 stainless steel. At high temperature, when the concentration of sulfuric acid is less than 15% and higher than 85%,316 stainless steel has a wide range of applications. 316 Stainless steel also has good chloride erosion properties, so it is usually used in the marine environment.

With the development of social economy, stainless steel pipe has been widely used. Will certainly bring new changes in various fields.

Theoretical Weight of Stainless Steel Tube: W= Outer Diameter - Wall Thickness x x0.02491. Wall Thickness

Category
The rolling method is divided into hot rolling, hot extrusion and cold drawing stainless steel pipe.
According to the metallographic structure of stainless steel, it is divided into semi-ferrite semi-m martensite stainless steel pipe, martensite stainless steel pipe, austenitic iron stainless steel pipe and so on.

Specification quality
A, GB14975-94< Stainless Steel Seamless Steel Pipe) The length of hot rolled steel pipe is 1.5~10 m, hot extruded steel pipe equal to and greater than 1 The wall thickness of cold-drawn (rolled) steel pipe is 0.5~1.0 mm ,1.0~7, and 1.5~8 m. if the wall thickness is greater than 1.0
B, diameter of hot rolled (hot extruded) steel pipe is 54~480 mm and the wall thickness is 4.5~45. The diameter of cold-drawn (rolled) steel pipe is 6~200 mm and the wall thickness is 0.5~21.
C, there shall be no cracks, folding, cracking, cracks, rolling, delamination and scarring defects on the inner and outer surfaces of the steel pipe, these defects shall be completely removed (except for pipes for machining) and the wall thickness and outer diameter shall not exceed the negative deviation after removal. Any other minor surface defects not exceeding the allowable negative deviation may not be removed.

D, straight path allows depth. hot-rolled, hot-extruded steel tubes of not more than 5% of nominal wall thickness with diameters less than and equal to 140 mm, maximum depth not greater than 0.5 mm; cold-drawn (rolled) steel tubes not greater than 4% of nominal wall thickness, maximum depth not greater than 0.3 mm.
E, both ends of the steel pipe should be cut into right angles and burr removed. Manufacturing process of stainless steel seamless pipe:
1. hot rolling (extruded seamless steel pipe): tube billet → heating → perforation → three-roll oblique rolling, continuous rolling or extrusion → pipe removal (or reduction), cooling, straightening → water pressure test (or flaw detection) and storage
The raw material of rolling seamless pipe is round tube billet. The round tube embryo is cut by cutting machine to process the billet with a growth degree of about 1 meter and sent to the furnace by conveyor belt for heating. The billet is heated into the furnace at a temperature of about 1200 degrees Celsius. The fuel is hydrogen or acetylene. Furnace temperature control is a key problem. After the round tube billet is out of the oven, it must pass through the pressure perforation machine to carry on the empty. The common perforator is conical roller perforator, which has high production efficiency, good product quality, large perforation diameter expansion and can wear many kinds of steel. After perforation, the round tube billet has been three-roll oblique rolling, continuous rolling or extrusion. After extrusion, take off the pipe and set the diameter. The diameter fixing machine rotates into the steel embryo through the conical bit at high speed to form the steel pipe. The inner diameter of the steel pipe is determined by the outer diameter length of the drill bit. After the steel pipe is fixed, it enters the cooling tower and is cooled by water spray. After cooling, the steel pipe will be straightened. The steel pipe is straightened and sent from conveyor belt to metal flaw detector (or hydraulic test) for internal flaw detection. If there are cracks, bubbles and other problems inside the steel pipe, it will be detected. Steel pipe quality inspection but also through strict manual selection. After quality inspection of steel pipe, spray the number, specification, production batch number and so on with paint. And crane into the warehouse.
2. Cold drawing (rolling) seamless steel pipe: pipe billet → heating → perforation → head → annealing → pickling → oiling (copper plating), multi-pass cold drawing (cold rolling)→ billet pipe heat treatment → straightening water pressure test (flaw detection) marking → storage.
The rolling method of cold drawn seamless steel pipe is more complicated than that of hot rolled seamless steel pipe. Their production process is basically the same in the first three steps. The difference starts from the fourth step, after the tube blank is empty, to hit the head, annealing. After annealing, special acid liquid should be used for pickling. After pickling, oil. Then followed by a multi-pass cold drawing (cold rolling) billet tube, special heat treatment. After heat treatment, same treatment as steel tube cooling process